Preparation and investigation of magnetic properties of MnNiTi-substituted strontium hexaferrite nanoparticles

Abstract

A series of M-type strontium hexaferrite powders with substitution of Mn2, Ni2 and Ti4 ions for Fe3 ions according to the formula SrFe9(Mn0.5-xNi xTi0.5)3O19, where x ranges from 0 to 0.5 with a step of 0.1, has been prepared via the conventional ceramic method. In order to get nanoparticles, the obtained powders were milled in a high energy SPEX mill for 1 h. XRD investigations of the unmilled and milled powders show that the prepared samples are all single phase hexaferrite. Lattice parameters and mean crystallite sizes of the powders were determined from the XRD data and Scherrer's formula. Transmission electron microscope (TEM) was used to analyze their structures. Room temperature magnetizations and coercivities of the samples in a magnetic field of 15 kOe have been determined from the hysteresis loops. It was found that magnetizations of the milled samples were smaller than the magnetization of the unmilled samples. This decrease, based on coreshell model, has been attributed to the presence of a magnetically dead layer on the particles' surface of the milled powders. In addition, the magnetizations of the milled samples decrease with the increase in x value. This decrease has been discussed according to site occupation of the substituted cations on the sublattices. The discussion also supports the increase of lattice parameters and the decrease of Curie temperature as x increases. © 2010 Elsevier B.V.