Single phase Zn2+-substituted magnetite nanocrystallites are synthesized via co-precipitation method and used as lithium-ion battery electrodes. The structural properties and vacancy distribution of nanoparticles are evaluated by X-ray diffraction, X-ray photoelectron spectroscopy (XPS), and positron annihilation lifetime spectroscopy (PALS). The Rietveld refinement of the X-ray diffraction patterns shows that the lattice constant increases with Zn2+ content from 8.392 Å for magnetite to 8.448 Å for Zn0.2Fe2.8O4. The XPS measurements show that cation vacancies increase with Zn content on the surface of nanoparticles. Positron annihilation lifetime spectra suggest more concentration of monovacancies and larger size of vacancy clusters in the Zn0.1Fe2.9O4 sample compared with the other two samples, Fe3O4 and Zn0.2Fe2.8O4. Electrochemical measurements show better reversibility, higher initial discharge capacity, and lower electrochemical impedance for the Zn0.1Fe2.9O4 electrode, which are attributed to the higher concentration of vacancy defects in its nanocrystallites. The electrochemical impedance spectroscopy (EIS) shows that the Li+ diffusion coefficient (DLi+) increases with Zn2+ doping from 1.51 × 10–15 cm2s–1 for Fe3O4 to 3.25 × 10–13 cm2s–1 for Zn0.1Fe2.9O4, and 1.43 × 10–13 cm2s–1 for Zn0.2Fe2.8O4. The initial discharge capacities of the samples found to be about 1345.04 mAh g−1 for Fe3O4, 1435.82 mAh g−1 for Zn0.1Fe2.9O4, and 1063.72 mAh g−1 for Zn0.2Fe2.8O4 electrodes, respectively. During first few cycles, the discharge capacity decline faster as Zn content increases. The discharge capacity of the Zn0.2Fe2.8O4 electrode is stable at 410 mAhg−1 from the 60th to the 200th cycle, which is higher than the Fe3O4 electrode (150 mAhg−1) and the Zn0.1Fe2.9O4 electrode (270 mAhg−1). This variance is explained by the cation vacancy concentration and the lattice constant of the samples. The impedance of the electrodes is also affected by the vacancy defects formed during the sample preparation. © 2024 Elsevier B.V.

Sendust Alloy: A Review on the Synthesis, Structure, Magnetic Properties, and Applications

( Article . )

Mozaffari, M., Amoohadi m.,

Physics of Metals and Metallography (0031918X)125(Suppl 1)

2023

Effect of Europium Substitution on the Structural, Magnetic and Relaxivity Properties of Mn-Zn Ferrite Nanoparticles: A Dual-Mode MRI Contrast-Agent Candidate

( Article . Green Published, gold )

Saeidi, Hamidreza, Mozaffari, Morteza, Ilbey, Serhat, Asanjarani, Neda, Saeidi, H., Mozaffari, M., Ilbey, S., Dutz s., , Zahn d., , Azimi gandomani, G., Bock, M.

Nanomaterials (20794991)13(2)

Magnetic nanoparticles (MNPs) have been widely applied as magnetic resonance imaging (MRI) contrast agents. MNPs offer significant contrast improvements in MRI through their tunable relaxivities, but to apply them as clinical contrast agents effectively, they should exhibit a high saturation magnetization, good colloidal stability and sufficient biocompatibility. In this work, we present a detailed description of the synthesis and the characterizations of europium-substituted Mn-Zn ferrite (Mn0.6Zn0.4EuxFe2-xO4, x = 0.00, 0.02, 0.04, 0.06, 0.08, 0.10, and 0.15, herein named MZF for x = 0.00 and EuMZF for others). MNPs were synthesized by the coprecipitation method and subsequent hydrothermal treatment, coated with citric acid (CA) or pluronic F127 (PF-127) and finally characterized by X-ray Diffraction (XRD), Inductively Coupled Plasma (ICP), Vibrating Sample Magnetometry (VSM), Fourier-Transform Infrared (FTIR), Dynamic Light Scattering (DLS) and MRI Relaxometry at 3T methods. The XRD studies revealed that all main diffraction peaks are matched with the spinel structure very well, so they are nearly single phase. Furthermore, XRD study showed that, although there are no significant changes in lattice constants, crystallite sizes are affected by europium substitution significantly. Room-temperature magnetometry showed that, in addition to coercivity, both saturation and remnant magnetizations decrease with increasing europium substitution and coating with pluronic F127. FTIR study confirmed the presence of citric acid and poloxamer (pluronic F127) coatings on the surface of the nanoparticles. Relaxometry measurements illustrated that, although the europium-free sample is an excellent negative contrast agent with a high r(2) relaxivity, it does not show a positive contrast enhancement as the concentration of nanoparticles increases. By increasing the europium to x = 0.15, r(1) relaxivity increased significantly. On the contrary, europium substitution decreased r(2) relaxivity due to a reduction in saturation magnetization. The ratio of r(2)/r(1) decreased from 152 for the europium-free sample to 11.2 for x = 0.15, which indicates that Mn0.6Zn0.4Eu0.15Fe1.85O4 is a suitable candidate for dual-mode MRI contrast agent potentially. The samples with citric acid coating had higher r(1) and lower r(2) relaxivities than those of pluronic F127-coated samples.